OK Flux 10.72
Agglomerated aluminate-basic flux for Submerged Arc Welding especially for applications with toughness requirements at low temperature. Excellent slag removal also in narrow V-joints. For wind tower productions, pressure vessels, general constructions etc. Extremely high current carrying capacity. For single or multi wire procedures. Suitable for DC and AC welding. Single layer and multi layer welding of unlimited plate thickness.
Luokittelut
| Luokka | S A AB 1 57 AC H5 |
| Nimi | EN ISO 14174 |
Hyväksynnät
| Hyväksynnät |
CE EN 13479 DB 51.039.12 |
| Hyväksynnät tehdaskohtaisia, lisätietoja ESABilta. |
Lisäaineen ominaisuudet
| Seostavuus | No Silicon and moderately Manganese alloying |
| Emäksisyys | nom: 1.9 |
| Tiheys | nom: 1.2 kg/dm3 |
| Vetypitoisuus | max 5 ml H/100g weld metal (Redried flux) |
| Raekoko | 0.315-2.0 mm (9x48 mesh) |
| Kuonatyyppi | Aluminate-basic |
Jauheenkulutus
| Jännite | Jauheen kulutus lankakiloa kohti DC+ | Jauheen kulutus lankakiloa kohti AC |
| 26 V | 0.7 kg | 0.6 kg |
| 30 V | 1.0 kg | 0.9 kg |
| 34 V | 1.3 kg | 1.2 kg |
| 38 V | 1.6 kg | 1.4 kg |
| A | Mitat | Siirtonopeus |
| 580 A | Ø 4.0 mm | 55 cm/min |
Luokittelut
| Lanka | AWS / EN | EN - Hitsatussa tilassa | AWS - hitsatussa tilassa | AWS - lämpökäsiteltynä |
| OK Autrod 12.24 | A5.23:EA2/ 14171-A:S2Mo; 24598-A:S S Mo | 14171-A: S 46 3 AB S2Mo | A5.23: F8A5-EA2-A3 | A5.23: F8P5-EA2-A3 |
| OK Autrod 12.22 | A5.17:EM12K/ 14171-A:S2Si | 14171-A: S 38 5 AB S2Si | A5.17: F7A8-EM12K | A5.17: F6P8-EM12K |
| OK Autrod 13.27 | A5.23:ENi2/ 14171-A:S2Ni2 | 14171-A: S 46 6 AB S2Ni2 | A5.23: F8A8-ENi2-Ni2 | A5.23: F7P8-ENi2-Ni2 |
| OK Autrod 12.20 | A5.17:EM12/ 14171-A:S2 | 14171-A: S 38 5 AB S2 | A5.17: F7A8-EM12 | A5.17: F6P8-EM12 |
| OK Autrod 13.64 | A5.23:EA2TiB/ 14171-A:S2MoTiB | A5.23: F8TA8-EA2TiB | ||
| OK Autrod 13.62 | A5.23:EG/ 14171-A:SZ3TiB | - | ||
| OK Autrod 13.24 | A5.23:ENi6/ 14171-A:S3Ni1Mo0,2 | - |
Hyväksynnät
| Lanka | CE | CWB | DB | DNV | GL | VdTÜV |
| OK Autrod 12.20 | * | - | * | - | - | * |
| OK Autrod 12.22 | * | * | * | * | * | * |
| OK Autrod 12.24 | * | - | * | - | - | * |
| OK Autrod 13.27 | * | - | - | - | - | - |
| *Jag tänkte lämna den bort. Jag tror Sverige har lämnat den bort också. För vi will inte styra kunder till ESAB.com och på webben finns inga fact sheet. |
Tyypilliset mekaaniset ominaisuudet
| Lanka | Tila | Myötöraja | Murtolujuus | Charpy V -iskusitkeys | Venymä |
| OK Autrod 12.20 | Hitsatussa tilassa AWS DC+ | 415 MPa (60 ksi) |
500 MPa (73 ksi) |
125 J @ -30°C, (93 ft-lb @ -30 °F) 70 J @ -50°C, (52 ft-lb @ -50 °F) 50 J @ -62°C, (37 ft-lb @ -62 °F) 125 J @ -30°C, (93 ft-lb @ -22 °F) 100 J @ -40°C, (74 ft-lb @ -40 °F) 70 J @ -50°C, (52 ft-lb @ -58 °F) 50 J @ -62°C, (37 ft-lb @ -79.6 °F) |
30 % |
| OK Autrod 12.20 | Hitsatussa tilassa EN AC | 420 MPa | 500 MPa (73 ksi) |
140 J @ -30°C, (104 ft-lb @ -22 °F) 130 J @ -40°C, (96 ft-lb @ -40 °F) 80 J @ -50°C, (59 ft-lb @ -58 °F) |
33 % |
| OK Autrod 12.22 | Hitsatussa tilassa AWS DC+ | 415 MPa (60 ksi) |
500 MPa (73 ksi) |
120 J @ -30°C, (89 ft-lb @ -30 °F) 100 J @ -40°C, (74 ft-lb @ -40 °F) 70 J @ -50°C, (52 ft-lb @ -50 °F) 50 J @ -62°C, (37 ft-lb @ -62 °F) 120 J @ -30°C, (89 ft-lb @ -22 °F) 70 J @ -50°C, (52 ft-lb @ -58 °F) 50 J @ -62°C, (37 ft-lb @ -79.6 °F) |
30 % |
| OK Autrod 12.22 | Hitsatussa tilassa EN AC | 425 MPa | 500 MPa (73 ksi) |
140 J @ -30°C, (104 ft-lb @ -22 °F) 130 J @ -40°C, (96 ft-lb @ -40 °F) 80 J @ -50°C, (59 ft-lb @ -58 °F) |
32 % |
| OK Autrod 12.24 | Hitsatussa tilassa AWS DC+ | 500 MPa (73 ksi) |
590 MPa (86 ksi) |
60 J @ -30°C, (44 ft-lb @ -30 °F) 40 J @ -40°C, (30 ft-lb @ -40 °F) 35 J @ -46°C, (26 ft-lb @ -46 °F) 60 J @ -30°C, (44 ft-lb @ -22 °F) 35 J @ -46°C, (26 ft-lb @ -50.8 °F) |
25 % |
| OK Autrod 12.24 | Hitsatussa tilassa EN AC | 535 MPa | 600 MPa (87 ksi) |
70 J @ -30°C, (52 ft-lb @ -22 °F) 50 J @ -40°C, (37 ft-lb @ -40 °F) 40 J @ -50°C, (30 ft-lb @ -58 °F) |
24 % |
| OK Autrod 13.24 | Hitsatussa tilassa AWS DC+ | 530 MPa (77 ksi) |
660 MPa (96 ksi) |
90 J @ 0°C, (67 ft-lb @ 32 °F) 35 J @ -40°C, (26 ft-lb @ -40 °F) |
28 % |
| OK Autrod 13.27 | Hitsatussa tilassa AWS DC+ | 490 MPa (71 ksi) |
610 MPa (88 ksi) |
100 J @ -40°C, (74 ft-lb @ -40 °F) 80 J @ -51°C, (59 ft-lb @ -51 °F) 50 J @ -62°C, (37 ft-lb @ -62 °F) 80 J @ -51°C, (59 ft-lb @ -59.8 °F) 50 J @ -62°C, (37 ft-lb @ -79.6 °F) |
30 % |
| OK Autrod 13.27 | Hitsatussa tilassa EN AC | 520 MPa (75 ksi) |
610 MPa (88 ksi) |
120 J @ -30°C, (89 ft-lb @ -22 °F) 100 J @ -40°C, (74 ft-lb @ -40 °F) 80 J @ -50°C, (59 ft-lb @ -58 °F) 60 J @ -60°C, (44 ft-lb @ -76 °F) |
27 % |
| OK Autrod 13.62 | Hitsatussa tilassa (acc. AWS) Plate thickness: 12mm; Heat Input: 2.2kJ/mm; Side 1: 600A, 32V, 53cm/min; Side 2: 700A, 60cm/min; DC+ | 500 MPa (73 ksi) |
610 MPa (88 ksi) |
50 J @ -62°C, (37 ft-lb @ -62 °F) 50 J @ -62°C, (37 ft-lb @ -79.6 °F) |
27 % |
| OK Autrod 13.64 | Hitsatussa tilassa (acc. to AWS) Plate thickness 12mm Heat input 2.2kJ/mm 700A, 32V, 60cm/min DC+ | 560 MPa (81 ksi) |
660 MPa (96 ksi) |
50 J @ -62°C, (37 ft-lb @ -62 °F) 50 J @ -62°C, (37 ft-lb @ -79.6 °F) |
27 % |
Hitsiaineen koostumus
| Hitsiaineen Koostumus | ||||||||||||||
| C | Mn | Mo | Ni | Si | ||||||||||
| OK Autrod 12.20 AC, 580A, 29V | ||||||||||||||
| 0.06 % | 1.4 % | - | - | 0.2 % | ||||||||||
| OK Autrod 12.20 DC+, 580A, 29V | ||||||||||||||
| 0.05 % | 1.5 % | - | - | 0.2 % | ||||||||||
| OK Autrod 12.22 AC, 580A, 29V | ||||||||||||||
| 0.06 % | 1.4 % | - | - | 0.3 % | ||||||||||
| OK Autrod 12.22 DC+, 580A, 29V | ||||||||||||||
| 0.05 % | 1.5 % | - | - | 0.3 % | ||||||||||
| OK Autrod 12.24 AC, 580A, 29V | ||||||||||||||
| 0.06 % | 1.5 % | 0.5 % | - | 0.2 % | ||||||||||
| OK Autrod 12.24 DC+, 580A, 29V | ||||||||||||||
| 0.05 % | 1.6 % | 0.5 % | - | 0.2 % | ||||||||||
| OK Autrod 13.27 AC, 580A, 29V | ||||||||||||||
| 0.07 % | 1.4 % | - | 2.2 % | 0.30 % | ||||||||||
| OK Autrod 13.27 DC+, 520A, 29V | ||||||||||||||
| 0.05 % | 1.4 % | - | 2.2 % | 0.30 % | ||||||||||